Xingtai Shineway Science & Technology company is a diversified carbon black company,focusing on Producing, R&D, innovating and marketing carbon black and Carbon Nanotubes(MWCNTS).
 |
SPECIFICATION
Item | Unit | Standard | ASTM Test Method |
Iodine Absorption Value | g/kg | 82±6 | ASTMD-1510 |
Oil Absorption Value | 10-5m3/kg | 72±6 | ASTMD-2414 |
Oil Absorption Value (Compressed) | 10-5m3/kg | 62-74 | ASTMD-3493 |
CTAB Absorption Surface Area | 103m2/kg | 74-86 | ASTMD-3765 |
STSA | 103m2/kg | 70-82 | ASTMD-6556 |
Nitrogen Absorption Surface Area | 103m2/kg | 72-84 | ASTMD-6556 |
Tint Intensity | % | 103-119 | ASTMD-3266 |
Heating Loss | % | ≤2.0 | ASTMD-1509 |
Ash | % | ≤0.7 | ASTMD-1506 |
45μm Sieve Residue | mg/kg | ≤1000 | ASTMD-1514 |
500μm Sieve Residue | mg/kg | ≤10 | ASTMD-1514 |
Impurities | - | 无 | —— |
Content Of Fine Powder | % | ≤10 | ASTMD-1508 |
Decantation Density | kg/m3 | 455±40 | ASTMD-1513 |
300% Stretching Stress | Mpa | -3.5±1.5 | ASTMD-3192 |
INTRODUTION
The N326 compound has high reinforcement and low heat-up. Compared to the compounds with other high abrasion furnace blacks, the N326 compound has lower tensile stress, lower elongation and similar tensile strength at break.The deficiency of the N326 compounds is lower tensile strength. abrasion and fatigue resistance.
APPLICATION
Carbon black N326 is used in the tread compounds with high strength and low heat-up. It is also used in the conveyor belt, seals and other high performance compounds, as well as color master batch. Carbon black N326 in the natural rubber compounds has similar physical-mechanical performance as channel black while the vulcanization rate is kept same. The compound filled with N326 has high tensile strength, crack resistance and abrasion.
SPECIFICATION
Item | Unit | Standard | ASTM Test Method |
Iodine Absorption Value | g/kg | 82±6 | ASTMD-1510 |
Oil Absorption Value | 10-5m3/kg | 72±6 | ASTMD-2414 |
Oil Absorption Value (Compressed) | 10-5m3/kg | 62-74 | ASTMD-3493 |
CTAB Absorption Surface Area | 103m2/kg | 74-86 | ASTMD-3765 |
STSA | 103m2/kg | 70-82 | ASTMD-6556 |
Nitrogen Absorption Surface Area | 103m2/kg | 72-84 | ASTMD-6556 |
Tint Intensity | % | 103-119 | ASTMD-3266 |
Heating Loss | % | ≤2.0 | ASTMD-1509 |
Ash | % | ≤0.7 | ASTMD-1506 |
45μm Sieve Residue | mg/kg | ≤1000 | ASTMD-1514 |
500μm Sieve Residue | mg/kg | ≤10 | ASTMD-1514 |
Impurities | - | 无 | —— |
Content Of Fine Powder | % | ≤10 | ASTMD-1508 |
Decantation Density | kg/m3 | 455±40 | ASTMD-1513 |
300% Stretching Stress | Mpa | -3.5±1.5 | ASTMD-3192 |
INTRODUTION
The N326 compound has high reinforcement and low heat-up. Compared to the compounds with other high abrasion furnace blacks, the N326 compound has lower tensile stress, lower elongation and similar tensile strength at break.The deficiency of the N326 compounds is lower tensile strength. abrasion and fatigue resistance.
APPLICATION
Carbon black N326 is used in the tread compounds with high strength and low heat-up. It is also used in the conveyor belt, seals and other high performance compounds, as well as color master batch. Carbon black N326 in the natural rubber compounds has similar physical-mechanical performance as channel black while the vulcanization rate is kept same. The compound filled with N326 has high tensile strength, crack resistance and abrasion.